Mn2+ Intercalated V2C MXene for Enhanced Sodium Ion Battery

WEI Shi-Qiang, WANG Chang-Da, ZHANG Peng-Jun, ZHU Ke-Fu, CHEN Shuang-Ming, SONG Li

Mn2+Intercalated V2C MXene for Enhanced Sodium Ion Battery

WEI Shi-Qiang, WANG Chang-Da, ZHANG Peng-Jun, ZHU Ke-Fu, CHEN Shuang-Ming, SONG Li

(National Synchrotron Radiation Laboratory, CAS Center for Excellence in Nanoscience, University of Science and Technology of China, Hefei 230029, China)

Mn2+intercalation strategy to optimize the sodium storage performance of V2C MXene was studied. The intercalated Mn2+not only enlarged the interlayer spacing of V2C MXene but also formed a V-O-Mn covalent bond, which was beneficial to stabilize the structure of V2C and inhibit the structural collapse caused by volume change during Na+decalation or intercalation. As a result, the intercalated V2C MXene (V2C@Mn) electrode showed a high specific capacity of 425 mAh·g–1at the current density of 0.05 A·g–1, and 70% retention after 1200 cycles. This result clearly suggests that cations intercalated MXene has a great prospect in Na+storage.

layered material; V2C Mxene; Na+storage; metal cation intercalation; XAFS

There is a growing desire to develop renewable and clean energy, due to environmental problems such as pollution caused by fossil fuels[1]. Sodium ion battery (SIB) is spurring rapid development as a substitute for lithium ion battery because of the abundance of Na resources, low cost and similar working mechanism[2-3]. However, the design of sodium ion devices with excellent properties is not easy as the lack of appropriate anode materials restricted by the larger radius of sodium ion than lithium ion (0.102 nm0.076 nm)[4]. This will result in sluggish kinetics of sodium ions and structural collapse of the electrode material during charge and discharge cycles. For instance, graphite, a commercialized lithium ion battery anode material, is not suitable for the negative electrode of SIB[5].

In recent years, some advancements have been made on the anode materials of Na ion battery. Like metal tin has been proved as high specific capacity anode material, but impeded its practical application due to huge volume change during its working process[6]. Transition metal carbides and nitrides (MXenes) are promising for energy storage since its discovery in 2011 in terms of its metallic electrical conductivity, large electrochemically active surface and unique layered structure[7-9].Currently, the most widely studied MXenes for Na+storage are Ti3C2[10-11]. However, it has been proved that V2C MXene is also one of the most promising electrode materials due to its smaller atomic mass[12]. Even though, only a few V2C MXene works for NIB are reported due to the difficulties in sample preparation and low capacity. For example, Yang,[13]reported the storage mechanism of sodium ion intercalation between interlayers of vanadium carbide with a small capacity about 125 mAh·g–1at 10 mA·g–1, which is still a gap between practical applications. Our previous works have proven that the Li+storage performance of V2C MXene can be improved by intercalation of cobalt and tin ions[14-15]. It paved a path to improve the performance of V2C based sodium ion battery in both specific capacity and cycle stability through metal cations intercalation.

In the present study, we reported the intercalation of transition metal ions of manganese into layered V2C MXene by ion exchange method, labeled as V2C@Mn. Mn2+was successfully decorated into the interlayer of V2C MXene and formed V-O-Mn bond according to the analysis of XRD, XAS, TEM and Element Mapping characterizations. It was demonstrated that the V2C@Mn electrodes exhibited high specific capacity and outstanding cycling performance for SIB.

1 Experimental

1.1 Synthesis of V2C and V2C@Mn MXenes

As discussed in our previous articles, V2C MXene was synthesized through selectively etching V2AlC MAX powders, which were synthesized by calcining the ball-milled V, Al and C powers under 1500 ℃ in argon atmosphere. To obtain K+intercalated V2C (V2C@K) MXene, about 500 mg as-prepared V2C powers were immersed in 20 mL 0.2 mol/L KOH aqueous solution followed by stirring for 2 d at 45 ℃. Afterwards, the solution was centrifuged by using deionized water and ethanol for several times. Then V2C@K was obtained after freeze-drying overnight. V2C@Mn was prepared by soaking V2C@K in 0.2 mol/L Mn(NO3)2through ion exchange between manganese ions and K+.

1.2 Material characterization

The morphology of V2C@Mn was presented with a field emission SEM (SU8220) and a TEM (JEOl JEM2010), elemental mapping images were also carried out with SEM (SU8220). X-ray diffraction (XRD) patterns were measured by a Sample horizontal high power X-ray diffractometer (Rigaku TTRIII) with Cu Kαradiation (=0.154 nm). Chemical compositions of V2C@Mn were analyzed by high-resolution XPS recorded with a Synchrotron Radiation Photoelectron Spectrometer Station Equipment in Hefei by using Mg Kα X-ray (=1253 eV). V L-edge and O K-edge XANES measurements were performed at the beamline BL12B-a (CMD) in Hefei Synchrotron Radiation Equipment. The Mn K-edge XAFS measurement was performed in the fluorescence mode at the beamline 1W1B in Beijing Synchrotron Radiation Facility (BSRF).

1.3 Electrochemical measurements

The working electrodes of V2C@Mn and V2C MXenes were prepared by mixing V2C@Mn or V2C MXene (70%), acetylene black (ACET 20%), and polyvinylidene fluoride (PVDF, 10%). Then it was coated on a copper foil after uniformly grinding in-methyl-2-pyrrolidone (NMP) and dried in vacuum oven overnight. The batteries were assembled in an Ar filled glove box (MBraun, Germany) into coin cells (CR2032) with sodium tablets as the counter electrodes, glass fiber as the separators and 1 mol/L NaClO4in (EC: DMC,. 1 : 1) as the electrolyte. Rate capability and cycle ability were achieved on a Land CT2001A cell test system at 25 ℃ in the potential range between 0.01 and 3 V. Meanwhile, cyclic voltammetry (CV) at scan rate from 0.1 to 1.0 mV·s-1in the same voltage range was performed on the CHI660D electrochemical workstation.

2 Results and discussion

2.1 Structure characterization

V2C powers were produced by selectively etching out the Al atomic layer from the MAX phase. During etching, the surface would be functionalized with hydroxyl, oxygen or fluorine terminations, so it has a formulation V2CT(T= F, O, OH). Transition metal ions of manganese entered the vanadium carbide layers by replacing the potassium ions which were intercalated into V2C MXene because of the etching effect of KOH. Manganese ions could shore up the layers of V2C MXenes during the charge and discharge process which could prevent the structural collapse and accelerate ion diffusion.

As illustrated in Fig. 1(a), the X-ray diffraction (XRD) image shows a typical (0002) peak of V2C MXene around 12° with some V2AlC residue after HF treatment. After stirring in KOH solution, the (0002) peak shifts toward lower degree, which implies the expansion of the V2C@K MXene interplaner. According to Bragg equation, the interlayer spacing of V2C@K MXene is about 0.96 nm. Interestingly, after the replacement of K+by Mn2+, the interlayer spacing of V2C@Mn decreases to approximately 0.95 nm compared with V2C@K. This weak contraction can be attributed to greater electrostatic attraction of bivalent Mn ion than monovalent K ion. Similar shrinkage is also observed in Co, Sn intercalated MXenes[14-15]. SEM image of V2C@Mn in Fig. 1(b) shows that the V2C@Mn preserved layer structure which is similar to the original structure of V2C, indicating that there is no obvious structure collapse after Mn ion intercalation. Elements mapping shows the uniform distribution of V, O and Mn. The layered structure of V2C@Mn is also presented in the HRTEM image (Fig. 1(c)), it shows a interlayer spacing of 0.95 nm which is consistent with XRD results. The ICP-AES indicates that the element composition of V, Al and K for V2C-KOH from ICP is 100.5, 1.765 and 8.683 μg·mL-1, corresponding to 70.70wt%, 1.20wt% and 6.11wt%, respectively. For V2C@Mn, the ICP results for V, Al, K and Mn atoms were 106.5, 1.529, 2.489 and 7.61 μg·mL-1, corresponding to 71.89wt%, 1.0wt%, 1.16wt% and 5.00wt%, respectively. It can be concluded that nearly all of K was successfully substituted by Mn, and few adsorptive or intercalated K ions remained. In short, manganese ions successfully intercalated into V2C MXene and enlarged the interlayer spacing which may stable the structure and accelerate ion transmission.

The intercalation of manganese ions was investigated by X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine spectroscopy (XAFS) as shown in Fig. 2. In the high resolution Mn2p spectrum, two predominant Mn2p3/2peaks are located at 641.3 and 643.2 eV, corresponding to divalent manganese ions and trivalent manganese ions[16]. Among them, divalent manganese ions account for the majority, and trivalent manganese ions have only a small part. It can be clearly verified by the Mn K-edge XANES results of V2C@Mn MXene and MnO as shown in Fig. 2(b). The absorption edge position of Mn K-edge XANES spectrum of V2C@Mn is very close to that of the MnO, which indicates that almost all of the manganese ions are divalent rather than trivalent. XPS and XAFS are powerful experimental technology for explanation the valence and spin states of transition- metal ion in the solids[17]. The former mainly gives the valence information within 10 nm of the material surface, while the latter gives the average information of the whole material. Thus, it can be concluded that most of the Mn2+are intercalated inside the interlayer, while some Mn3+located on the near surface of V2C MXene because of the easier oxidation. The corresponding Fourier- transformed EXAFS spectra in Fig. 2(c) clearly displays the Mn-O peak of V2C@Mn compared with MnO, indicating the formation of Mn-O bond.

Fig. 1 Mophological characterization of V2C@Mn

(a) XRD patterns of V2C, V2C-K and V2C@Mn; (b) SEM image of as-prepared V2C@Mn; (c) TEM image of as prepared V2C@Mn; (d) Elements mapping of V2C@Mn, from left to right: scanning area map of V, O and Mn

Fig. 2 Structural characterization of V2C@Mn MXene

(a) High resolution XPS of manganese; (b) Spectra of XANES for V2C@Mn MXene and MnO standard sample; (c) Fourier-transformed Mn K-edge EXAFS spectra of V2C@Mn MXene and MnO standard sample; (d) V L-edge and O K-edge XANES spectra of pure V2C MXene and V2C@Mn MXene

To study more detailed electronic structure information of V2C@Mn, V L-edge and O K-edge XANES spectra were performed (Fig. 2(d)). For the V L-edge, there are two peaks located at 518 and 525 eV, corresponding to the spin-orbit (SO) spilt L3(2p3/2) and L2(2p1/2) parts, respectively. It is obvious that the shape of two curves are very similar except that the peak position shifted to higher energy after Mn2+intercalation. As we know, this shift refers to the elevated valence of V ions. Due to crystal field splitting, the O K-edge can divided into two parts. The first part is the region of O2p-V3d(t2g) and O2p-V3d(eg) at lower energy. The second part is the region at higher energy about 542 eV, associated with the mixture of O2p with V4sp[18-19]. The O2p orbitals are greatly mixed with V3d orbitals, resulting in a wide distribution and strong absorption signal which clearly demonstrates the significant covalent nature of the V–O bonds in the V2C and V2C@Mn MXene. After Mn2+interaction, the energy of second part shifted to lower position because of the transitions toward hybridized levels between Mn4sp and V–O hybridization[20], corresponding to the observed shift of V edge to a higher energy. This indicates the formation of Mn–O bonds. Therefore, combining with all of the above analysis results we can convince the conformation of V–O–Mn bond in V2C@Mn MXene.

2.2 Na ion storage performance

In order to evaluate the electrochemical properties of the Mn2+intercalated V2C as anode material for NIB, 2032 coin-type cells with Na foil as counterparts were assembled. Fig. 3(a) shows the cyclic voltammetry (CV) graph of V2C@Mn MXene electrode at scan rate from 0.1 to 1.0 mV·s–1.At low scan rate 0.1 mV·s–1, there are a pair of wide redox peaks at approximately 1.5/1.8 V after the initial cycle. As the sweep rates increased, the redox peaks become more pronounced. More intuitively, all the CV curves display a quasi-rectangle shape, which indicates a typical pseudocapacitive behavior of V2C MXene for NIB. In order to add more persuasive insight, we calculated thefrom anodic and cathodic currents. Thefrom anodic and cathodic currents are about 0.75 and 0.79 respectively, clearly indicating the storage mechanism is mainly pseudocapacitive behavior. Our CV result is similar to other works where V2C MXene also shows pseudo-capacitive behavior in Na+storage[21]. The high and irreversible cathodic current below 1 V might be ascribed to the formation of solid electrolyte interphase (SEI) and the decomposition of electrolyte in the first cycle[22].

Fig. 3 Electrochemical performance in half-cell

(a) CV curves of V2C@Mn MXene electrode at the scan rate from 0.1 to 1.0 mV·s–1; (b) Rate performance of V2C@Mn and pure V2C electrodes at different current densities; (c) Charge and discharge profiles of V2C@Mn at different current densities; (d) Cycle stabilities of V2C@Mn and pure V2C electrodes at the current density of 1000 mA·g–1.Inset in (a) is the variation of lgversus lg

To meet the demand of fast charge and release of energy storage devices, the rate and cycle performance of devices are extremely important. As shown in Fig 3(b), the V2C@Mn electrode not only delivers higher specific capacity than pure V2C electrode, but also shows better rate performance. Even under high current density of 5 A·g–1, V2C@Mn electrode can still deliver a capacity of 60 mAh·g–1, but for V2C electrode, it is only about 50 mAh·g–1. Fig. 3(c) shows the charge and discharge curves of V2C@Mn MXene at current densities from 0.05 to 5 A·g–1. There are about 425, 280, 170, 120, 86 and 56 mAh·g–1under 0.05, 0.1, 0.5, 1, 2, 5 A·g–1, respectively. The shapes of charge and discharge curves are approximate slash and there are no platforms with the increase of current densities, which were consistent with CV results. The behavior demonstrates that the Na+storing mechanism of V2C@Mn MXene is mainly capacitive behavior and with the current density increases, the contribution of capacitance also increases. More intuitively, the superiority of V2C@Mn MXene to V2C MXene is reflected in the cycle stability. After rate performance test, both of the two electrodes are carried on cycling test as shown in Fig. 3(d). There is still 70% of discharge capacity remained after 1200 long-term cycles for V2C@Mn electrode. In contrast, the specific capacity of pure V2C electrode decays very fast, only 20% capacity is preserved after 800 cycles. The higher specific capacity, more excellent rate performance and superior cycle stability of V2C@Mn are benefited from the intercalation of Mn2+into V2C MXene layers which stables the structure and accelerates ion transmission.

The dynamics of intercalated Mn2+was investigated byX-ray photoelectron spectroscopy (XPS) at different charge and discharge voltages. As shown in Fig. 4, the intensity of the peaks corresponding to Mn2+are weakened as the charging voltage increased while the peaks corresponding to Mn3+increase, indicating that Mn2+is oxidized to Mn3+during charging process. On the contrary, the Mn3+is reduced to Mn2+during discharging process. It can concluded that Mn ions intercalation strategy not only stabilizes the structure of V2C MXene, but also increases the pseudo-capacity.

3 Summary

In summary, Mn2+intercalated V2C MXene was successfully synthesized through ion exchange method. By using XRD, element mapping, XPS, and XAFS characterization techniques, it can be proved that the intercalated Mn2+not only enlarged the interlayer spacing of V2C MXene but also formed a V–O–Mn covalent bond in the interlayer, which were beneficial to improve the Na+storage capacity and stabilize the structure of V2C MXene volume change. The results showed that V2C@Mn electrode can deliver a high specific capacity of 425 mAh·g–1at current density of 0.05 A·g–1. Notably, over 70% capacity was still remaining after 1200 long-term cycles. We believe that ion intercalation can promote the highly development of MXene based Na+storage.

Fig. 4 Ex-situ X-ray photoelectron spectroscopy at different charge and discharge voltages

[1] LUO J M, FANG C, JIN C B,. Tunable pseudocapacitance storage of MXene by cation pillaring for high performance sodium- ion capacitors., 2018, 6(17): 7794–7806.

[2] LUO J M, ZHENG J H, NAI J W,. Atomic sulfur covalently engineered interlayers of Ti3C2MXene for ultra-fast sodium-ion storage by enhanced pseudocapacitance., 2019, 29(10): 1808107.

[3] KAJIYAMA S, SZABOVA L, SODEYAMA K,. Sodium-ion intercalation mechanism in MXene nanosheets., 2016, 10(3): 3334–3341.

[4] DONG Y, WU Z S, ZHENG S H,. Ti3C2MXene-derived sodium/ potassium titanate nanoribbons for high-performance sodium/po­tassium ion batteries with enhanced capacities.,2017, 11(5): 4792–4800.

[5] LUO W, SHEN F, BOMMIER C,. Na-ion battery anodes: materials electrochemistry., 2016, 49(2): 231–240.

[6] ZHANG Y, ZHU P, HUANG L,. Few-layered SnS2on few-layered reduced graphene oxide as Na-ion battery anode with ultralong cycle life and superior rate capability., 2015, 25(3): 481–489.

[7] ANASORI B, LUKATSKAYA M R, GOGOTSI Y. 2D metal carbides and nitrides (MXenes) for energy storage.,2017, 2: 16098.

[8] PENG J H, CHEN X Z, ONJ W J,. Surface and heterointerface engineering of 2D MXenes and their nanocomposites: insights into electro- and photocatalysis., 2018, 5: 1–33.

[9] KHAZAEI M, RANJBAR A, ARAI M,. Electronic properties and applications of MXenes: a theoretical review.,2017,5: 2488–2503.

[10] ER D, LI J, NAGUIB M,. Ti3C2MXene as a high capacity electrode material for metal (Li, Na, K, Ca) ion batteries., 2014, 6(14): 11173–11179.

[11] LI J, YAN D, HOU S,. Improved sodium-ion storage performance of Ti3C2TMXenes by sulfur doping., 2018, 6(3): 1234–1243.

[12] ZHU J J, SCHWINGENSCHLÖGL U. P and Si functionalized MXenes for metal-ion battery applications., 2017, 4: 025073.

[13] BAK S M, QIAO R M, YANG W L,. Na-ion intercalation and charge storage mechanism in 2D vanadium carbide., 2017, 7(20): 1700959.

[14] WANG C D, XIE H, CHEN S M,. Atomic cobalt covalently engineered interlayers for superior lithium-ion storage., 2018, 30(32): 1802525.

[15] WANG C D, CHEN S M, XIE H,. Atomic Sn4+decorated into vanadium carbide MXene interlayers for superior lithium storage., 2019, 9(4): 1802977.

[16] DU Y, HUA Z, HUANG W,. Mesostructured amorphous manganese oxides: facile synthesis and highly durable elimination of low-concentration NO at room temperature in air., 2015, 51(27): 5887–5889.

[17] KANG J S, HWANG J, KIM D H,. Soft X-ray magnetic circular dichroism study of valence and spin states in FeT2O4(T=V, Cr) spinel oxides.,2013, 113(17):17E116.

[18] YE Y F, KAPILASHRAMI M, CHUANG C H,. X-ray spectroscopies studies of the 3d transition metal oxides and applications of photocatalysis., 2017, 7(1): 53–66.

[19] JANG W L, LU Y M, CHEN C L,. Local geometric and electronic structures of gasochromic VOfilms., 2014, 16(10): 4699–4708.

[20] FILATOVA E O, BARABAN A P, KONASHUK A S,. Transparent-conductive-oxide (TCO) buffer layer effect on the resistive switching process in metal/TiO2/TCO/metal assemblies., 2014, 16(11): 113014.

[21] DALL’AGNESE Y, TABERNA P L, GOGOTSI Y,. Two-dimensional vanadium carbide (MXene) as positive electrode for sodium-ion capacitors., 2015, 6(12): 2305–2309.

[22] GE Y, PAN P F, PENG X,. Dual-confined sulfur cathodes encapsulated in MnO2nanotubes and wrapped with PEDOT for high-performance lithium-sulfur batteries., 2019, 39(5): 769–779.

Mn2+插层V2C MXene应用于钠离子电池的研究

魏世强, 王昌达, 张鹏军, 朱可夫, 陈双明, 宋礼

(中国科学技术大学 中国科学院纳米科学卓越中心, 国家同步辐射实验室, 合肥 230029)

本研究提出一种Mn2+插层策略用于优化V2C MXene的储钠性能。Mn2+的插层不仅扩大了V2C MXene的层间距同时形成了V-O-Mn 共价键, 有利于稳定V2C的结构, 抑制Na+脱嵌过程中由于体积变化引起的结构坍塌。结果表明, 插层后的V2C MXene(V2C@Mn)电极在电流密度为0.05 A·g–1时具有425 mAh·g–1的高比容量, 并且经过1200次长循环后容量还有70%保留。V2C@Mn优异的性能表明阳离子插层调控的MXene在Na+存储方面具有潜在的应用前景。

层状材料; V2C MXene; 钠离子存储; 金属阳离子插层; 同步辐射吸收谱

TQ174

A

2019-06-03;

2019-07-15

National Key R&D Program of China (2017YFA0303500); National Natural Science Foundation of China (11574280, 21727801, 11605201, U1632151); National Postdoctoral Program for Innovative Talents (BX 20190315); NSFC-MAECI (51861135202); CAS Key Research Program of Frontier Sciences (QYZDB-SSW-SLH018); Fundamental Research Funds for the Central Universities (WK2310000074)

WEI Shi-Qiang(1994–), male, Master candidate. E-mail: sqw@mail.ustc.edu.cn

魏世强(1994–), 男, 硕士研究生. E-mail: sqw@mail.ustc.edu.cn

CHEN Shuang-Ming, associate professor. E-mail: csmp@ustc.edu.cn

陈双明, 副研究员. E-mail: csmp@ustc.edu.cn

1000-324X(2020)01-0139-06

10.15541/jim20190270