Defect engineering on all-inorganic perovskite solar cells for high efficiency

Bingcheng Yu ,Chuantian Zuo ,Jiangjian Shi ,Qingbo Meng ,and Liming Ding,

1Beijing National Laboratory for Condensed Matter Physics,Institute of Physics,Chinese Academy of Sciences,Beijing 100190,China

2Center for Excellence in Nanoscience (CAS),Key Laboratory of Nanosystem and Hierarchical Fabrication (CAS),National Center for Nanoscience and Technology,Beijing 100190,China

3Center of Materials Science and Optoelectronics Engineering,University of Chinese Academy of Sciences,Beijing 100049,China

4School of Physical Sciences,University of Chinese Academy of Sciences,Beijing 100049,China

5Songshan Lake Materials Laboratory,Dongguan 523808,China

Perovskite solar cells based on organic–inorganic hybrid perovskite materials have become a research hotspot in photovoltaics field due to their outstanding power conversion efficiency (PCE)[1].Nonetheless,the organic cations are volatile and have rotation freedom,which is not good for photoand thermal-stability of the devices.Fortunately,these issues can be solved by all-inorganic perovskites,which consist of Cs,Pb and I (or Br)[2,3].Moreover,the all-inorganic perovskites,such as CsPbI3,are excellent candidates as top-cell absorbers in tandem solar cells because of their suitable bandgaps and high stability.All-inorganic perovskites were first used as light absorbers in solar cells in 2015[4,5].All-inorganic perovskite solar cells experienced rapid development in last few years,and the PCE reaches 20.4% at the end of 2020[6].Most recently,Menget al.pushed the PCE to >21.0%(unpublished).Despite these advances,we should recognize that there still remains a big gap between the PCEs for all-inorganic perovskite solar cells and hybrid perovskite solar cells(Fig.1(a))[7,8].The PCE for hybrid cells has reached 80% of the theoretical limit,while the PCE for all-inorganic cells is still below 70% of the theoretical limit[9].A detailed analysis on performance parameters of these cells suggests that the PCE for all-inorganic cells is mainly limited by the open-circuit voltage (Voc) and fill factor (FF) (Fig.1(b)).In solar cells,these two parameters correlate to non-radiative charge loss caused by defects[10].Therefore,defect engineering is the most critical approach for achieving higher PCE for all-inorganic perovskite solar cells.

Though CsPbI3has similar bulk defects to that of hybrid perovskites (Fig.1(c))[11],it presents more charge recombination and much shorter carrier lifetime.All-inorganic perovskites might have a higher degree of atom (or lattice) disorder and defect distribution because the crystals experience complicated phase transformation processes under relatively high temperature.Thus,improving the crystallization of allinorganic perovskites is an effective approach to reduce the defects[6,12,13].Recently,Seoket al.controlled the intermediate stages during the crystallization process by adding methyl ammonium chloride[6].CsPbI3films showed high crystallinity and good surface morphology.Thermally stimulated current test indicated that the defect density decreased from 3.947 × 1016to 2.803 × 1016cm–3.With surface passivation,CsPbI3solar cells gave a PCE of 20.37%.At the same time,Menget al.added NH4I into perovskite precursor solution to adjust the nucleation and crystallization,thus reducing the defects (Fig.1(d))[13].Thermal admittance spectroscopy showed that the charge capture in crossing the perovskite was reduced by about one order of magnitude.Recently,Menget al.controlled perovskite crystallization by using coordination-active additives or synergistic additives,and the solar cells delivered a PCE of over 21.0%.

Another defect suppression strategy is element doping at the Pb site in perovskite.The 6s and 6p orbitals of Pb2+significantly contribute to the energy band of CsPbX3(X=Cl,Br and I) perovskites,and using divalent metal ions (i.e.Cu2+,Mn2+and Sn2+) doping or alloying Pb sites will affect the defect tolerance[14].Recently,Liuet al.found that Mn2+incorporation could passivate the defects at the grain boundary and surface,thus reducing carrier recombination (Fig.1(e))[15].

Surface passivation is widely used for enhancing the performance of all-inorganic perovskite solar cells[16].Bulky organic ammonium halides,such as quaternary ammonium salt,were used to passivate the defects in hybrid perovskites.This method can also be used to passivate the surface defects of all-inorganic perovskites.In 2018,Zhaoet al.treated CsPbI3film with choline iodide to reduce surface defects[17].Phenyltrimethylammonium halides and 3,3-diphenylpropylamine were used for surface passivation,accelerating the development of all-inorganic perovskite solar cells[18,19].The recently reported high PCE of 20.37% benefited from the surface passivation by octylammonium iodide[6].Organic materials having Coulombic interaction with the terminal atoms of perovskites can be applied for surface or interface passivation.Yeet al.theoretically and experimentally proved that an amino-functionalized polymer and a dopant-free hole-transporting polymer can help passivating both the top and the bottom surface of CsPbI2Br films (Fig.1(f))[20].The numerous organic ligands synthesized for enhancing the luminescence of all-inorganic perovskite nanocrystals may be suitable for passivating perovskite surface and grain boundaries[21,22].

In summary,all-inorganic perovskites have a complicated formation process and large lattice distortion caused by phase competition.Besides the top surface,more attention should be paid to passivating the defects at bottom surface and inside the bulk.Interface materials which can withstand high temperature should be developed to buffer the energy level mismatch,lattice mismatch,and interface stress between inorganic charge-transport layers and all-inorganic perovskites.

Acknowledgements

This work was supported by the National Natural Science Foundation of China (51872321,11874402,52072402,51627803) and the National Key Research and Development Program of China (2018YFB1500101).L.Ding thanks the National Key Research and Development Program of China(2017YFA0206600) and the National Natural Science Foundation of China (51773045,21772030,51922032,21961160720)for financial support.