以电化学方法在离子液体[DEME][BF4]中合成铂纳米粒子

2018-02-01 06:56刘丽来李明仙潘晓娜赵艳红张锦秋安茂忠杨培霞
无机化学学报 2018年2期
关键词:比克哈尔滨化学

王 丹 刘丽来 李明仙 潘晓娜 赵艳红 张锦秋 安茂忠 杨培霞*,

(1哈尔滨工业大学化工与化学学院,工业和信息化部新能源转化与储存关键材料技术重点实验室,哈尔滨 150001)

(2黑龙江科技大学环境与化学工程学院,哈尔滨 150022)

(3深圳比克动力电池有限公司,深圳 518119)

As a promising catalyst,Pt has been widely used for decades due to its high catalytic activity in oxygen reduction reaction,hydrogen oxidation reaction,alcohol and acid oxidation reaction for fuel cells as well as organic reactions for petroleum chemistry.On account of the high cost of platinum,it is significant to reduce the particle size to improve electrochemical active area and utilization of the platinum.Platinum particles can be produced by the method of chemical reduction[1-2], impregnation[3],microemulsion[4],microwave assisted[5-6], electrodeposition[7-11], magnetron sputtering[12-13]and some other methods.Electrodeposition method is a low cost and environmentally friendly way to synthesis most metals compared to other methods.Hence,there are some studies on the electrodeposition of platinum in aqueous solution[7-8,14],and the results show that it is difficult to obtain a few nanometers of platinum nanoparticles in aqueous solution. In addition,electrodeposition in aqueous solution is often accompanied with hydrogen evolution reaction,resulting in the emergence of pinholes on the coating,which can seriously affect the coating performance.

Therefore,electrodeposition in the nonaqueous solution shows its advantages and necessity.In recent years,ionic liquids have attracted intensive attention as new possible solvents for fabrication of both noble metals and non-noble metals due to its many advantages[15-16],such as a wide electrochemical window,high ionic conductivity,good thermal stability,and etc.

In order to obtain more smaller and uniform Pt nanoparticles,there are some efforts have been made to deposit Pt in ionic liquids.Some researchers investigated the electrodeposition of platinum in 1-nbutyl-3-methylimidazolium tetrafluoroborate([BMIM][BF4])[17], 1-n-butyl-3-methylimidazolium hexafluorophosphate ([BMIM][PF6])[17-18]and N,N-diethyl-N-methyl-N-(2-methoxyethyl)ammonium tetrafluoroborate([DEME][BF4])[19].These are mainly focused on the electrodeposition behavior of Pt,and the investagation about the catalytic performance of Pt,which electrodeposited in ionic liquids,is still rare.

In this study, electrodeposition of Pt nanoparticles was carried out on a glassy carbon electrode in [DEME][BF4]containing chloroplatinic acidhexahydrateat60℃.Andthecatalytic performance of Pt nanoparticles was also investigated.The mean size of as prepared Pt nanoparticles is estimated to be ca.2.38 nm,which also exhibit good catalytic performance.

1 Experimental

1.1 Materials

[DEME][BF4] was purchased from Shanghai Chengjie Chemical Co.,Ltd.The ionic liquid was dried under vacuum at a temperature of 80℃for more than 24 h before using.H2PtCl6·6H2O and H2SO4were obtained from Sinopharm Group Chemical Reagent Co.,Ltd.Both of them were analytical grade and used without further purification.

1.2 Methods

The electrodeposition was performed by a threeelectrode system.Glassy carbon (GC,Φ=3 mm)was used as a working electrode (WE).A Pt wire (Φ=0.5 mm)acted as the quasi-reference electrode and a Pt foil(1.2 cm×1.2 cm)served as counter electrode (CE).A constant potential was applied to the working electrode for 480 s to generate Pt nanoparticles on the GC at 60℃.

1.3 Characterization and testing

The catalytic test was also proceeded by a threeelectrode system,in which Pt supported on GC acted as WE,Saturated calomel electrode (SCE)and Pt foil served asRE and CE,respectively.Thecyclic voltammetry measurements were also carried out by a three electrode system,and the only difference was that a Pt wire was used as a quasi-reference electrode.All of the electrochemical measurements were carried out on a CHI750D electrochemical workstation.The microstructure of the Pt particles was characterized by scanning electron spectroscope (SEM,SU8010,Hitachi,15 kV),transmission eletron microscope (TEM,Tecnai G2 F20 S-TWIN,FEI,200 kV),high-resolution transmission electron microscope (HRTEM,200 kV)and selected area electron diffraction (SAED).

2 Results and discussion

2.1 Micromorphology of the Pt particles

SEM images of the Pt nanoparticles obtained at different electrodeposition potential are showed in Fig.1.When the potential is negatively shifted from-2.0 to-2.5 V,the particles are more uniform,and become smaller at-2.8 V.According to the metal electrodeposition theory,the nucleation rate is greater than the growth rate with the cathode overpotential increasing so that it can obtain smaller and dense deposition.The particle size of Pt particles is obviously larger when the potential is-3.0 V,which is due to apparently agglomeration of the nanoparticles.

Fig.1 SEM images of the Pt nanoparticles obtained in[DEME][BF4]containing 30 mmol·L-1H2PtCl6by potentiostatic electrodeposition at 60℃for 600 s with different potentials

The morphologies of Pt particles deposited for different deposition time are shown in Fig.2.When the deposition time is 120 s,the obtained particles are less and dispersed.The particles deposited for 300 s are uniformly distributed,but become more locally stacked and agglomerated when the deposition time increases to 480 s.As shown in Fig.2,a dense deposition was formed due to lengthen deposition time to 600 s causing the particles serious agglomeration.It is obvious that the agglomeration of the particles becomemoreseriouslywith thedeposition time increasing.

Fig.3 shows TEM images and the size distribution of Pt nanoparticles.The Pt nanoparticles obtained at the two different electrode potentials are both well dispersed and uniform.The average sizes (in diameter)of the Pt nanoparticles obtained by electrodeposition at-2.5 and-3.0 V are estimated to be 2.38 and 3.10 nm,respectively.It has been reported that when the particle size of platinum nanoparticles is 2.5~3.5 nm,the electrocatalytic activity of platinum catalyst can be greatly improved[20].Hence,it can be speculated that the prepared nanoparticles have good electrocatalytic activity.

Fig.2 SEM images of the Pt nanoparticles obtained in[DEME][BF4]containing 30 mmol·L-1H2PtCl6by potentiostatic electrodeposition with-2.5 V at 60℃for different times

Fig.3 Transmission electron microscopy and size distribution of the Pt nanoparticles obtained in[DEME][BF4]containing 30 mmol·L-1H2PtCl6 by potentiostatic electrodeposition at 60℃for 480 s with different potentials

2.2 Crystal structure of Pt

In order to investigate the microstructure of Pt nanoparticles more closely,the HRTEM images and SAED patterns of the catalysts are presented in Fig.4.The HRTEM image of Pt nanoparticles shown in Fig.4a demonstrates clear lattice fringes with an inter fringe distance of 0.221 nm corresponding to the lattice spacing of Pt(111)plane.The HRTEM image shown in Fig.4b displays the inter fringe distance of approximately 0.196 nm analogous to the Pt(200)plane.Its SAED pattern reveals the face-centered cubic(fcc)Pt crystal structure,which is indexed as (111),(200),(220)and (311)lattice planes of Pt.

Fig.4 HRTEM images and SAED patterns of Pt nanoparticles obtained in[DEME][BF4]containing 30 mmol·L-1H2PtCl6by potentiostatic electrodeposition with-2.5 V at 60℃for 480 s

2.3 Electrocatalytic evalution of Pt

To electrochemically evaluate the platinum nanoparticles,the CV curve of as prepared GC/Pt electrode were conducted with potential scanned from-0.25 to 1.25 V (SCE),as shown in Fig.5.Hydrogen adsorption and desorption curve each containing two separate peaks is due to the exposure of the different crystal planes of platinum nanoparticles[21-22].The catalytic peaks of Pt(110)and (100)planes gradually exposed with the scanning progress.The peak at about-0.07 V originates from the hydrogen adsorption/desorption on the Pt (100)plane,and its intensity reflects the fact that how many Pt(100)planes are present on the surface of nanoparticles[23].These results demonstrate that the Pt nanoparticles prepared at-2.5 V are relatively enriched in Pt(110)and (100)planes,when these planes are compared.This is consistent with the results of the HRTEM images and SAED patterns in Fig.4.The crystal planes of Pt nanoparticles can greatly affect the electrocatalytic activity of the surface[24].Accordingly,these results demonstrate that the prepared catalyst has good electrocatalytic performance.Of course,it′s also need to make some efforts on optimizing the electrocatalytic performance of the Pt nanoparticles.

Fig.5 Cyclic voltammogram curve of GC/Pt electrode obtained in[DEME][BF4]containing 30 mmol·L-1 H2PtCl6by potentiostatic electrodeposition at-2.5 V (vs Pt)in 0.5 mol·L-1H2SO4with a scan rate of 50 mV·s-1

2.4 Electrodeposition behavior of Pt

Fig.6 displays the cyclic voltammogram of the GC electrode in[DEME][BF4] (Fig.6a)and[DEME][BF4]containing 30 mmol·L-1H2PtCl6(Fig.6b).As shown in Fig.6,the ionic liquid is relatively stable in the range of the potential from 1.5 to-3.5 V (vs Pt).When the potential is negatively shifted to-3.5 V (vs Pt),the decomposition of the cation [DEME]+begins to occur,and becomes seriously after-4.1 V (vs Pt).As can be seen from Fig.6b,there are two reduction peaks in the negative scanning process.The first reduction peak c1appears at the potential of-0.8 V (vs Pt)and the second reduction peak c2appears at-1.7 V (vs Pt).It′s possibly corresponding to the two-step reduction of chloroplatinic acid[19].The first step is the process of reduction of Ptビ to Ptギ at-0.8 V (vs Pt),and the second step is the process of Ptギ to Pt at-1.7 V (vs Pt).In thepositive scanning process,only one oxidation peak a1occurs at-0.4 V (vs Pt),which corresponds to the oxidization of Ptギ to Ptビ.However,the area of peak a1is small compared with the reduction peaks.It′s likely to be that some of the[PtCl4]2-is reduced to Pt metal when the potential is negatively shifted during the scanning process.

Fig.6 Cyclic voltammograms of the GC electrode in different electrolytes at 60℃ with a scan rate of 50 mV·s-1

The CV curves at different scan rates were carried outto have an in-depth study on the electrodeposition behavior of platinum.Fig.7 displays the CV curves of[DEME][BF4]containing 30 mmol·L-1H2PtCl6at 60 ℃ with a sacn rate of 10,20,40,60,80,100 mV·s-1,respectively.If a reaction is a reversible reaction,the peak potential Epwill maintain constant because of the different scan rates.But for irreversible reactions,the peak potential Epwill move.In Fig.7,the scan rate increases from 10 to 100 mV·s-1,and the second reduced peak potential (c2)Epis negatively shifted.It indicates that the reaction of Ptギto Pt is an irreversible reaction[25-27].

The fitting equation of curve (1)and curve (2)obtained according to the peak c1and c2are y=0.368x+0.677,y=0.361x+0.964,respectively.From the fitting formula and Fig.7,it is obvious that jpand v1/2have a good linear relationship and the fitting curve does not go through the origin,indicating that the processes of Ptビ reduced to Ptギ and Ptギreduced to Pt are both controlled by diffusion process and electrochemical process together.

Fig.7 (a)Cyclic voltammograms of the GC electrode in[DEME][BF4]containing 30 mmol·L-1H2PtCl6 at 60 ℃ with different scan rates;(b)Fitting curve of peak current density jpand v1/2

3 Conclusions

In conclusion,platinum nanoparticles with a mean size of ca.2.38 nm were prepared via a potentiostatic electrodeposition method on a glassy carbon electrode from [DEME][BF4]at-2.5 V.The HRTEM imagesandcyclicvoltammogram curve confirm that the Pt nanoparticles show relatively high catalytic performance due to its (110)and (100)planes.Likewise,it is confirmed that the two-step reduction of Ptビis controlled by diffusion process and electrochemical process together.However,the catalytic performance should be improved further.It′s necessary to optimize the electrodeposition process of the Pt nanoparticles in the further research.

[1]Antoniassi R M,Otubo L,Vaz J M,et al.J.Catal.,2016,342:67-74

[2]Pullamsetty A,Sundara R.J.Colloid Interface Sci.,2016,479:260-270

[3]Zhang J,Yi X B,Liu S,et al.J.Phys.Chem.Solids,2017,102:99-104

[4]Pajic'M N K,Stevanovic'S I,Radmilovic'V V,et al.J.Solid State Electrochem.,2016,20(12):3405-3414

[5]Chu Y Y,Wang Z B,Gu D M,et al.J.Power Sources,2010,195:1799-1804

[6]Bharti A,Cheruvally G,Muliankeezhu S.Int.J.Hydrogen Energy,2017,42(16):11622-11631

[7]Liu S,Wang J Q,Zeng J,et al.J.Power Sources,2010,195(15):4628-4633

[8]Hsieh C T,Wei J M,Lin J S,et al.Catal.Commun.,2011,16(1):220-224

[9]Ye F,Wang T T,Li J J,et al.J.Electrochem.Soc.,2009,156(8):B981-B985

[10]Ruengkit C,Tantavichet N.Thin Solid Films,2017,636(31):116-126

[11]Zhang Y Y,Li F P,Liu X Q,et al.Electrochim.Acta,2017,242:165-172

[12]Hussain S,Erikson H,Kongi N,et al.Int.J.Hydrogen Energy,2017,42(9):5958-5970

[13]Alexeeva O K,Fateev V N.Int.J.Hydrogen Energy,2016,41(5):3373-3386

[14]Fouda-Onana F,Guillet N,AlMayouf A M.J.Power Sources,2014,271:401-405

[15]Endres F,Bukowski M,Hempelmann R,et al.Angew.Chem.Int.Ed.,2003,42(29):3428-3430

[16]Abbott A P,McKenzie K J.Phys.Chem.Chem.Phys.,2006,8(37):4265-4279

[17]He P,Liu H T,Li Z Y,et al.J.Electrochem.Soc.,2005,152(4):E146-E153

[18]Yu P,Qian Q,Wang X,et al.J.Mater.Chem.,2010,20(28):5820-5822

[19]Zhang D,Chang W C,Okajima T,et al.Langmuir,2011,27(23):14662-14668

[20]Giordano N,Passalacqua E,Pino L,et al.Electrochim.Acta,1991,36(13):1979-1984

[21]Solla-Gullón J,Vidal-Iglesias F J,Rodriguez P,et al.J.Phys.Chem.B,2004,108(36):13573-13575

[22]Markovic N,Gasteiger H,Ross P N.J.Electrochem.Soc.,1997,144(5):1591-1597

[23]Wang C,Daimon H,Onodera T,et al.Angew.Chem.Int.Ed.,2008,47(19):3588-3591

[24]Markovic N M,Gasteiger H A,Ross Jr P N.J.Phys.Chem.,1995,99(11):3411-3415

[25]Xiaowei Y,Maozhong A,Yunwang Z,et al.Electrochim.Acta,2011,58:516-522

[26]YANG Xiao-Wei(杨潇薇),ZHANG Yun-Wang(张云望),AN Mao-Zhong(安茂忠),et al.Chinese J.Inorg.Chem.(无机化学学报),2012,28(12):2617-2625

[27]Jayakumar M,Venkatesan K A,Srinivasan T G.Electrochim.Acta,2007,52(24):7121-7127

猜你喜欢
比克哈尔滨化学
哈尔滨“8·25”大火 烧出了什么
星空下的向日葵
奇妙的哈尔滨之旅
长信科技挑战借壳底线
奇妙的化学
奇妙的化学
刘派
奇妙的化学
发力于“芯”比克耀动广州国际新能源汽车展
奇妙的化学